Hongzhang Pan, Yongmei Zhu and Mingjiang Fang
Maraging steel is the material of deep sea pressure equipment. The characteristics of corrosion fatigue crack initiation in 18Ni (250) were investigated by performing a tensile fatigue test under different loading conditions. The mechanism of corrosion f...
ver más
|
|
|
|
|
|
|
Yicheng Yang, Jiaqi Chang, Zhaoguo Mi and Weihua Yang
Radial cracks appear in the labyrinth seal fins of the shrouded turbine blade of an aero-engine during service. To clarify the influence rule of rubbing force on crack initiation, a high-speed rubbing test bench and a numerical calculation model are esta...
ver más
|
|
|
|
|
|
|
Yicheng Yang, Zhaoguo Mi, Wencan Zhang, Jiaqi Chang, Yongjun Liu, Bintao Zhong and Weihua Yang
The labyrinth-honeycomb seals have been widely used in aero-engine. However, radial cracks appear on labyrinth seal fins of shrouded turbine blade in use. To clarify the rubbing mode of radial crack initiation, a high-speed rubbing test bench was designe...
ver más
|
|
|
|
|
|
|
Jürgen Bär
The direct current potential drop method (DCPDM) is widely used to determine the crack length in fatigue experiments. In practice, some special features of this method must be considered. Aside from general information on the experimental setup and calib...
ver más
|
|
|
|
|
|
|
Jun Wu, Wen Wang, Minghui Lu and Yu Hu
A metal fatigue damage model is established in this study by employing real-time strain monitoring to evaluate the damage state of metal materials. The fatigue life simulation, based on crystal plasticity finite element analysis, establishes the constitu...
ver más
|
|
|
|
|
|
|
Juntao Ma, Xue Ling, Qin Zhou, Zhiqiao Wang and Hongjie Liu
In order to study the mechanism of crack propagation in rock cutting, experiments and discrete element numerical simulation of rock cutting at different depths were adopted in this paper. The rock fragmentation can be divided into mini-size fragmentation...
ver más
|
|
|
|
|
|
|
Kasumi Morita, Masashi Mouri, Riccardo Fincato and Seiichiro Tsutsumi
This paper investigates the fatigue cyclic deformation behavior of mid-carbon steel. Uniaxial tensile loading tests and fatigue tests under constant and multi-step amplitude loading steps are performed to characterize the influence of loading history. Th...
ver más
|
|
|
|
|
|
|
Emi Kawai, Hideki Kakisawa, Atsushi Kubo, Norio Yamaguchi, Taishi Yokoi, Takashi Akatsu, Satoshi Kitaoka and Yoshitaka Umeno
For design of multi-layered environmental barrier coatings (EBCs), it is essential to assure mechanical reliability against interface crack initiation and propagation induced by thermal stress owing to a misfit of the coefficients of thermal expansion be...
ver más
|
|
|
|
|
|
|
Abdelwahab Zerrouki, Abdelkader Boulenouar, Mohamed Mazari, Mohamed Benguediab
Pág. 110 - 117
In this paper, an experimental and a numerical analysis were carried out using High density polyethylene (HDPE). Sheets with an initial central crack (CCT specimens) inclined with a given angle are investigated and compared to the loading direction. The ...
ver más
|
|
|
|
|
|
|
Federico Nunez, Sidney Guralnick, Thomas Erber
Pág. Page 135 - 146
series of SEM micro-graphs were obtained from the cracked surfaces of samples from two types of AISI-1018 steel after applying fatigue tests at a stress ratio ofR=-1. Various strain-control levels were used in the range ±0.0008 = ? = ±0.0014 following a ...
ver más
|
|
|
|
|
|
|
Kinoshita, K.,Arakawa, S.
Pág. 68 - 74
For fatigue assessment, recently effective notch stress (ENS) approach is accepted as a valid alternative to fracture mechanics approaches in Japan. However, at least one study showed that the fatigue assessment at weld root of load-carrying crucif...
ver más
|
|
|
|
|
|
|
Kai Liu, Fangli Wang, Wei Pan, Le Yang, Shuwei Bai, Qiang Zhu and Mingbo Tong
In order to determine the average behavior time of widespread fatigue damage (WFD) in an aircraft multi-site damage (MSD) structure and complete the fatigue analysis of WFD sensitive parts, this paper adopts a probabilistic method to analyze the crack in...
ver más
|
|
|
|
|
|
|
Stefan Ritter and Hans-Peter Seifert
Low-alloy reactor pressure vessel steels have a rather low susceptibility to stress corrosion cracking (SCC) in a boiling water reactor (BWR) environment if the high-temperature water contains no anionic impurities. Recent investigations revealed that un...
ver más
|
|
|
|
|
|
|
Xiulan Bao, Biyu Chen, Peng Dai, Yishu Li and Jincheng Mao
Walnut shell breaking is the first step of deep walnut processing. This study aims to investigate the mechanical properties and fracture state of the Qingxiang walnut shell under unidirectional load and guide the complete separation of the walnut shell a...
ver más
|
|
|
|
|
|
|
Jan Patrick Sippel and Eberhard Kerscher
Understanding the mechanisms leading to very high cycle fatigue is necessary to make predictions about the behavior under various conditions and to ensure safe design over the whole lifetime of high-performance components. It is further vital for the dev...
ver más
|
|
|
|
|
|
|
Wansen Guo, Jinshen Wang, Chao Shi, Jianhong Chen, Wenhui Zeng, Guoxiao He and Kunying Ding
On the aero-engine combustor liner, a phenomenon of overheating resembling a hot spot exists, accompanied by a preferential peeling of the YSZ thermal barrier coating that will negatively affect the service life of the component. The hot spot temperature...
ver más
|
|
|
|
|
|
|
Amir Poursaee and Brandon Ross
The majority of works in the field of chloride-indued corrosion of steel in concrete are focused on the cracks formed by the corrosion products. However, the number of studies on the influence of cracks (pre-cracked concrete) on corrosion is limited. Cra...
ver más
|
|
|
|
|
|
|
Mulian Zheng, Peng Li, Jiangang Yang, Hongyin Li, Yangyang Qiu and Zhengliang Zhang
Previously published studies have proposed fatigue life prediction models for dense graded asphalt pavement based on flexural fatigue test. This study focused on the fatigue life prediction of High Modulus Asphalt Concrete (HMAC) pavement using the local...
ver más
|
|
|
|
|
|
|
Naseer Muhammad Khan, Liqiang Ma, Muhammad Zaka Emad, Tariq Feroze, Qiangqiang Gao, Saad S. Alarifi, Li Sun, Sajjad Hussain and Hui Wang
The brittleness index is one of the most integral parameters used in assessing rock bursts and catastrophic rock failures resulting from deep underground mining activities. Accurately predicting this parameter is crucial for effectively monitoring rock b...
ver más
|
|
|
|
|
|
|
Rasoul Najafi Koopas, Natalie Rauter and Rolf Lammering
Methodologies are developed for analyzing failure initiation and crack propagation in highly heterogeneous concrete mesostructures. Efficient algorithms are proposed in Python to generate and pack geometric features into a continuous phase. The continuou...
ver más
|
|
|
|