Resumen
Tungsten-modified hydrogenated amorphous carbon coatings (a-C:H:W) were deposited on high speed steel by reactive magnetron sputtering of a tungsten carbide target in an argon-ethine atmosphere. The deposition parameters, sputtering power, bias voltage, argon and ethine flow rate, were varied according to a central composite design comprising 25 different parameter combinations. For comparison, a tungsten carbide coating was deposited, as well. During coating deposition, the process variables, total pressure, sputtering voltage and bias current, were measured as process characteristics. The thickness of the deposited coatings was determined using the crater grinding method, and the deposition rate was calculated. Young?s modulus E and indentation hardness HIT were characterized by means of nanoindentation. With E = 80