Resumen
The aim of this study was to evaluate the effect of surface treatment and storage time on immediate repair bond durability of methacrylate- and ormocer-based bulk fill composites. In total, 265 discs were divided into 32 groups (n = 8/group) according to: (1) Material: X-tra fil and Admira Fusion X-tra; (2) Surface treatment: oxygen inhibition; matrix; Futurabond M+; Silane/Futurabond M+; Admira Bond; Silane/Admira Bond; ceramic repair system; and Silane/Cimara bond; and (3) Storage time: 24 h and 6 months. Each disc received three micro-cylinders from the same material. Specimens were subjected to micro-shear bond strength testing either at 24 h or 6 months. Data were analyzed using ANOVA/Tukey?s test/Student t-test (p = 0.05). All experimental factors had significant effect on bond strength (p < 0.0001). Drop in bond strength was noticed in both materials after six months (p < 0.05), except for Admira Fusion X-tra treated with silane/cimara adhesive (p = 0.860). Both materials showed insignificant values with Admira bond either at 24 h or 6 months (p = 0.275 and p = 0.060, respectively). For other treatments, X-tra fil showed significantly higher values at 24 h and 6 months (p < 0.05). Ceramic repair system can be used to immediately repair both methacrylate- and ormocer-based composites.